 Super translucency monolithic zirconium oxide materials/ ST zirconia discs/1200mpa zirconia/bloomden zirconia block/zirconia milling block/zirconia puck/zirconia ceramic block/dental zirconia block/For making contour/zolid/ prettau zirconia discs/ST zirconia blank/ST puck
Translucency: 41%
Flexural strength after sintering(Mpa): 1200Mpa
Sintering temperature (℃): 1480-1530

Model Number:ST
Certification:CE,ISO
Minimum Order Quantity:1 pcs
Packaging Details:Stardard packing ,Brand packing , OEM, According to the customer's demand , etc
Delivery Time:1-7days
Payment Terms:T/T, L/C, PayPal, Western Union, Alipay
Supply Ability:10000pcs monthly


Contact us
  • Description
  • Applications
  • Specifications
  • Competitive Advantage

Bloomzir® Super Translucent ST White is made of super translucent zirconium oxide(with 42% translucency), that guarantees natural tooth looking. With high flexural strength( 1200Mpa).

For Bloomzir® Super Translucent ST White, we recommend our bloomden color liquids(VITA 16 colors). With much better compatibility,you can get a perfect teeth.

Bloomzir® Super Translucent ST White Shade Range: VITA® 16 shades:

Bloomzir® Super Translucent ST White sintering illurstration:

1. Room temperature to 900°C (1652°F),  5°C/min, approximately by 180mins.

2. 900°C (1652°F) to 1530°C (2786°F), 8°C/min, approximately by 60mins.

3. Holding 1530°C (2786°F) for 120mins. 

4. Dropping from 1530°C (2786°F) to 900°C (1652°F), 5°C/min, approximately by 120mins.

5. Natural cooling

Bloomzir® Super Translucent ST White dental case by Dr. Andy Lee, a Tree Oral Inc.

Perfectly suitable for
* High aesthetic monolithic crowns and bridges (up to 3 units),small bridges and large bridges are available
* Especially for monolithic anterior restorations (bridges up to 3 units)
* High aesthetic veneering

Chemical composition

Components

ST

ZrO2+HfO2+Y2O3

≥99%

Y2O3

4.5%-6.0%

Al2O3

0.25%

Other Oxides

0.15

Physical characteristics


Properties

ST

Density before sinteringg.cm-3

3.10-3.20

Density after

sinteringg.cm-3

6.08-6.10

CTE(25-500℃)(K-1)

10.5

Flexural strength

after sintering(Mpa)

1200

Accelerated aging surface monoclinic phase content

15%

Light transmittance

44%

Chemical solubility after sintering(μg.cm-2)

100

Cytotoxicity

0 Level

Radioactivity(Bq.g-1)

0.1

Sintering temperature(℃)

1480-1530

Milling system

Specification

 Open CADCAM

98x10

98x12

98x14

98x16

98x18

98X20

98X22

98X25

Amann Girrbach Ceramill CADCAM

ZI71XS  12mm

ZI71X   14mm

ZI71    16mm

ZI71M   18mm

ZI71L   20mm

ZI71XL  25mm

Zirkonzahn M1/M3/M5

95x10

95x12

95x14

95x16

95x18

95X20

95X22

95X25



1.We are government authorized  R&D team cooperated with Local famous Hunan university' science and technology sector.
2.All of our blanks are isostatically pressed to insure a uniform density and shrinkage through the sintering process. In-house test capabilities include microhardness and flexural strength.
3.Specializing in manufacturing zirconia more than 10 years with strong production and deep in zirconia technology from powder to manufacturing
4.Sophisticated experience technician
5.Raw material approved FDA
6.Prompt delivery time ,stock available and warehouse more than 2000 ㎡.
7.Professional sales person replied within 24hours
8.Variety of payment method , T/T / Paypal / Via Ali pay Trade Assurance guarantee customers’ rights and interests.
9.When customers are not satisfied with merchandise, should be promptly returned or replacement within 7 days

Contact Us