Ultra Translucent UT White

Quick Detail

Ultra translucency high aesthetic veneering zirconium oxide materials/ zolid/ prettau zirconia discs/650mpa block/Dental Zirconia block, Dental Zirconia Disc, Dental Zirconia Blank/For making anterior solid
Light Transmittance: 49%
Flexural strength after sintering(Mpa): 650Mpa
Sintering temperature (℃): 1435-1450

Model Number:UT zirconia block
Certification:CE,ISO
Minimum Order Quantity:1 pcs
Packaging Details:Stardard packing ,Brand packing , OEM, According to the customer's demand , etc
Delivery Time:1-7days
Payment Terms:T/T, L/C, PayPal, Western Union, Alipay
Supply Ability:10000pcs monthly


Contact us
  • Description
  • Applications
  • Specifications
  • Competitive Advantage

Bloomzir® Ultra Translucent UT White is made of ultra tranclucent zirconium oxide (with 49% light transmittance), that guarantees natural tooth looking. With extreme flexural strength( 650Mpa). 


We recommend our bloomden color liquids. With much better compatible.

Bloomzir® Ultra Translucent UT White Shade Range: VITA®  9 shades:

Bloomzir® Ultra Translucent UT White sintering illurstration:

1. Room temperature to 900°C (1652°F),  5°C/min, approximately by 180mins.

2. 900°C (1652°F) to 1450°C (2642°F), 8°C/min, approximately by 60mins.

3. Holding 1450°C (2642°F) for 120mins. 

4. Dropping from 1450°C (2642°F) to 900°C (1652°F), 5°C/min, approximately by 120mins.

5. Natural cooling

Below is the case of Bloomzir® Ultra Translucent UT White 

Perfectly suitable for
* High aesthetic monolithic crowns and bridges (up to 3 units)
* Especially for monothic anterior restorations (bridges up to 3 units)
* High aesthetic veneering

Compatibility

* 98mm with a 10mm step. Compatible with Weiland, VHF, Roland, and most open CAD CAM Milling Machines.
* 95mm. Compatible with Zirkonzahn milling machines.
* AG89*71mm. Compatible with Amann Girrbach milling machines

1.Chemical composition

Components

UT

ZrO2+HfO2+Y2O3

99%

Y2O3

9%-10%

Al2O3

0.05

Other Oxides

0.05

2.Physical characteristics

Properties

UT

Density before sinteringg.cm-3

3.15-3.25

Density after

sinteringg.cm-3

6.05-6.07

CTE(25-500)(K-1)

10.5

Flexural strength

after sintering(Mpa)

650

Accelerated aging surface monoclinic phase content

15%

Light transmittance

49%

Chemical solubility after sintering(μg.cm-2)

100

Cytotoxicity

0 Level

Radioactivity(Bq.g-1)

0.1

Sintering temperature()

1435-1450

Milling system

Specification

 Open CADCAM

98x10

98x12

98x14

98x16

98x18

98X20

98X22

98X25

Amann Girrbach Ceramill CADCAM

ZI71XS  12mm

ZI71X   14mm

ZI71    16mm

ZI71M   18mm

ZI71L   20mm

ZI71XL  25mm

Zirkonzahn M1/M3/M5

95x10

95x12

95x14

95x16

95x18

95X20

95X22

95X25


1.We are government authorized  R&D team cooperated with Local famous Hunan university' science and technology sector.
2.All of our blanks are isostatically pressed to insure a uniform density and shrinkage through the sintering process. In-house test capabilities include microhardness and flexural strength.
3.Specializing in manufacturing zirconia more than 10 years with strong production and deep in zirconia technology from powder to manufacturing
4.Sophisticated experience technician
5.Raw material approved FDA
6.Prompt delivery time ,stock available and warehouse more than 2000 ㎡.
7.Professional sales person replied within 24hours
8.Variety of payment method , T/T / Paypal / Via Alipay Trade Assurance guarantee customers’ rights and interests.
When customers are not satisfied with merchandise, should be promptly returned or replacement within 7 days

Contact Us